Rankin, Jon E, Hill, Michael R, and Hackel, Lloyd A
Materials Science and Engineering A-Structural Materials Properties Microstructure and Processing, vol 349, iss 1-2
laser peening, residual stress, surface treatment, and fatigue
This paper reports measurements of the distribution of residual stress with depth from the surface in laser peened coupons made of a high-strength aluminum alloy. Residual stresses were measured using slitting (also known as the crack compliance method). Measurements were made on several coupons to: compare laser peening (LP) and shot peening (SP) residual stresses; ascertain the influence of LP parameters on residual stress; determine whether tensile residual stress existed outside the peened area; assess the variation of residual stress with in-plane position relative to the layout of the laser spots used for peening; and, determine the importance of a uniform spatial distribution of laser energy within the spot. Residual stress 0.1 mm from the surface due to LP and SP were comparable and the depth of the compressive stress for LP was far greater than for SP. Variations of most LP parameters did not significantly alter residual stress at shallow depths, but greater laser energy and larger layer overlap increased residual stress at depths between 0.2 and 0.6 mm from the surface. Residual stresses adjacent to the peened area were found to be compressive. Decreased levels of surface residual stress were found when laser spots had a non-uniform distribution of laser intensity. (C) 2002 Elsevier Science B.V. All rights reserved.